[1]解庆范,陈宾军,焦周平.贝壳粉负载磷钼杂多酸催化剂的制备及性能[J].泉州师范学院学报,2020,(06):6-12.
 XIE Qingfan,CHEN Binjun,JIAO Zhouping.The Preparation and Properties of Phosphomolybdic Heteropoly Acid Catalyst Supported onShell Powder[J].,2020,(06):6-12.
点击复制

贝壳粉负载磷钼杂多酸催化剂的制备及性能()
分享到:

《泉州师范学院学报》[ISSN:1006-6977/CN:61-1281/TN]

卷:
期数:
2020年06期
页码:
6-12
栏目:
化学与生命科学
出版日期:
2020-12-15

文章信息/Info

Title:
The Preparation and Properties of Phosphomolybdic Heteropoly Acid Catalyst Supported onShell Powder
文章编号:
1009-8224(2020)06-0006-07
作者:
解庆范陈宾军焦周平
泉州师范学院 化工与材料学院,福建 泉州 362000
Author(s):
XIE QingfanCHEN BinjunJIAO Zhouping
School of Chemical Engineering and Materials, Quanzhou Normal University, Quanzhou Fujian 362000,China
关键词:
贝壳粉 磷钼杂多酸 光催化氧化 废水处理
Keywords:
shell powder phosphomolybdic acid photocatalyticoxidation wastewater treatment
分类号:
O643.36
文献标志码:
A
摘要:
利用在600 ℃下煅烧的贝壳粉为负载体,采用浸泡法,制备负载型磷钼杂多酸催化剂,通过单因素实验,研究样品浸泡液浓度、处理时间、H2O2的用量、料液比等8个因素对刚果红模拟染料废水降解效果的影响.实验结果表明:浸泡液浓度为5 mmol/L的磷钼杂多酸溶液制备的0.01 g样品催化剂,在0.4 mL H2O2、pH=4、反应温度45 ℃左右以及搅拌的条件下,催化剂对刚果红的去除率较高,当溶液浓度为20 mg/L时去除率高达99%; 在最佳条件下,负载型杂多酸催化氧化降解刚果红染料废水的反应符合准二级反应.
Abstract:
The shell powder calcined at 600 ℃ was used as the carrier to prepare thesupported phosphomolybdic heteropoly acid catalyst by soaking method.Through single factorexperiment,the influences of eight factors, such as the concentration of the samplesoaking solution,treatment time,the amount of hydrogen peroxide(H2O2),the ratio ofmaterial to liquid,on the degradation effect of Congo red simulated dye wastewater werestudied.The results showed the removal rate of Congo red by catalyst was very high,reaching 99% when the solution concentration was 20 mg/L under the conditions of 0.4 mLH2O2, pH=4,reaction temperature around 45 ℃ and stirring with 0.01 g sample catalystprepared with 5 mmol/L molybdenum-phosphorous heteropolyacid solution.Under the optimumconditions, the catalytic oxidation of Congo red dye waste water by supported heteropolyacid was in accordance with the quasi-secondorder reaction.

参考文献/References:

[1] 王敏.多金属氧酸盐的合成、表征及其催化性能研究[D].上海:华中师范大学,2007.
[2] 李莉.高效复合光催化材料的设计制备及其催化性能研究[D].长春:东北师范大学,2009.
[3] 崔金玉,杨平雄.用溶胶-凝胶法制备的Cu2Bi2Cr2O8薄膜及其光学和铁磁性能研究[J].红外,2018,39(12):8-11.
[4] 黄燕霞.CsxPW11O39M(H2O)/TiO2纳米管复合材料的制备及可见光催化性能研究[D].海口:海南师范大学,2019.
[5] 刘树鑫.TiO2-AC催化剂的制备与处理染料废水的实验研究[J].供水技术,2018,12(6):22-25.
[6] 王伟平,张义军,杨水金.杂多酸光催化降解染料废水的研究进展[J].化工文摘,2009(4):52-55.
[7] 侯珊,刘向春.新型光催化剂钨酸锌的制备及性能改性研究进展[J].材料导报,2019,33(5):1541-1548.
[8] 李亚红,赵彬侠,张凯.H2O2催化湿式氧化酸性红B染料废水的研究[J].榆林学院学报,2011,21(4):63-65.
[9] MARTINS T,HERRMANN H,CHOI W,et al.Time-resolved microwave conductivity(TRMC)and size quantization[J].J Chem Soc Faraday Trans,1994,90:3315-3322.
[10] 陈金媛.高效二氧化钛/膨润土复合材料的制备及光催化性能研究[J].化学学报,2003,61(8):1311-1315.
[11] 蒋德敏,黄美英,方荣美,等.分光光度法测定水样中偶氮染料刚果红[J].分析试验室,2017,36(3):264-268.

备注/Memo

备注/Memo:
收稿日期:2020-09-16
作者简介:解庆范(1965—),女,黑龙江鹤岗人,教授,主要从事配位化学及废水处理研究.
基金项目:泉州师范学院大学生创新创业训练计划资助项目(201810399113)
更新日期/Last Update: 2020-12-15